700Amp class of HTS current lead Fabrication

700A급 고온초전도 전류도입선 제조

HTS tubes were fabricated in terms of various SrSO4 additions by Centrifugal Forming Method. For powder melting by induction, the optimum temperature ranges of melting and preheating were 105$0^{\circ}C$~110$0^{\circ}C$ and 55$0^{\circ}C$ for 30min respectively The mould rotating speed was 1000rpm. A tube was annealed at 84 $0^{\circ}C$ for 72 hours in oxygen atmosphere. The plates like grains more than 20${\mu}{\textrm}{m}$ were well developed along the rotating direction of mould regardless of the amounts of SrSO4 in Bi2212. The measured Ic and Jc at 77K(B = 0T) in Bi2212 with 7％ SrSO4 composition were about 680A and 380A/$\textrm{cm}^2$.