Abstract
Laves phases of $NdFe_2$, $Nd{(Fe_{0.5})}_2$, $SmCo_2$ and $Sm{(Fe_{0.5}Co_{0.5})}_2$ stoichiometry were prepared using a rapid solidification technology. Low temperature magnetic properties show ferromagnetic behaviors for the $Nd{(Fe_{0.5}Co_{0.5})}_2$, $SmCo_2$ and $Sm{(Fe_{0.5}Co_{0.5})}_2$Nd(Feo,Coo,) Laves compounds while a sort of spin reorientation has been suggested for the supposed composition of $NdFe_2$ alloy. This rapidly solidified $NdFe_2$ alloy is believed to consist of metastable rhombohedral $NdFe_7$ phase plus fine particles of Nd-rich phase. Some evidence of phase transition from the mixture of unstable $NdFe_7$ compound plus Nd-rich to $Nd_2Fe_{17}$ plus Fe-Nd-O phase was obtained after annealing the $NdFe_2$, alloy. The pseudo-binary Laves compound, $Sm{(Fe_{0.5}Co_{0.5})}_2$ exhibits a high coercivityof 4 kOe at room temperature with Curie temperature of $400^{\circ}C$ while the $Nd{(Fe_{0.5}Co_{0.5})}_2$ compound shows a magnetic moment of $2.8\;{\mu}_B/f.u.$.
$NdFe_2$, $Nd{(Fe_{0.5})}_2$, $SmCo_2$ 및 $Sm{(Fe_{0.5}Co_{0.5})}_2$ 조성의 Laves 화합물을 급속냉각기술에 의하여 제조하였다. 저온자기특성을 조사한 결과 $Nd{(Fe_{0.5}Co_{0.5})}_2$, $SmCo_2$와 $Sm{(Fe_{0.5}Co_{0.5})}_2$ 조성의 Laves 화합물은 강자성의 거동을 보이며 결정구조는 모두 C15의 단일상으로 존재하였으며, $NdFe_2$ 조성의 급냉합금은 일종의 spin reorientation 거동을 보였다. $NdFe_2$ 조성의 급냉합금은 화학조성식 $NdFe_7$의 준안정상과 Nd-rich상으로 구성됨을 알았다. $NdFe_2$ 급냉합금을 열처리 하면 $NdFe_7$은 $Nd_2Fe_{17}$과 Nd-Fe-O상으로 변태하였다. $Sm{(Fe_{0.5}Co_{0.5})}_2$ Laves 화합물의 보자력은 상온에서 4kOe이며 큐리온도는 $400^{\circ}C$로 측정된다. 또한 $Nd{(Fe_{0.5}Co_{0.5})}_2$ Laves 화합물은 상온에서 $2.8\;{\mu}_B/f.u.의$ 자기모멘트를 보유한다.