A Study on the Magnetic Properties of Amorphous Fe-Co-RE-B (RE=Nd, Sm, Gd, Tb) Alloys

비정질 Fe-Co-Re-B(RE=Nd, Sm, Gd, Tb) 합금의 자기적 성질

The temperature-dependent magnetization curves of amorphous Fe-Co-(Nd, Sm, Gd, Tb)-B alloys were measured using a vibrating sample magnetometer from 77 K up to 900 K. The spin wave stiffness constants and the range of the exchange interaction were calculated from the saturation magnetization values at 0 K. Curie temperatures and the Bloch coefficients estimated from the saturation magnetization curves. The low temperature dependence of magnetization is in good agreement with Bloch relation, $M_{s}(T)=M_{s}(O)(1-BT^{3/2}-CT^{5/2})$. The spin wave stiffness constant and the range of exchange interaction are decreased by substitution of heavy rare earth (Tb, Gd).

희토류-3d 천이원소인 비정질${[{(Fe_{80}CO_{20})}_{0.98}RE_{0.02}]}_{80}B_{20}(RE=Nd,\;Sm,\;Gd,\;Tb)$ 합금 리본시료에 대한 자기적 성질을 조사하기 위하여 시료진동형 자력계(vibrating sample magnetometor)를 이용하여 77 K부터 900 K까지의 온도 영역에서 포화자화 값을 온도의 함수로 측정 한후, Curie 온도 ($T_{c}$)와 Bloch 상수등을 추정하였다. 이들로 부터 spin wave stiffness 상수, 교환상호작용(exchange interaction)의 범위와 평균자승거리($$)등을 계산하였으며 각 희토류 원소에 대한 치환효과를 비교 분석하였다.