The Effects of Hexamethoxymethylmelamine on the Adhesion of Rubber to Brase-Plated Steel Cord

Hexamethoxymethylmelamine이 고무-황동피복코드간의 접착에 미치는 영향

  • Kim, Wan-Young (Department of Chemical Technology, College of Engineering, Chonbuk National University) ;
  • Kim, Youn-Sop (Department of Chemical Technology, College of Engineering, Chonbuk National University) ;
  • Yug, Gyeong-Chang (Department of Chemical Technology, College of Engineering, Chonbuk National University) ;
  • Kim, Hyung-Soon (Department of Chemical Technology, College of Engineering, Chonbuk National University) ;
  • Lee, Jeong-Yong (Department of Electronic Material Engineering, Korea Advanced Institute of Science and Technology) ;
  • Choi, Sang-Won (Dept. of Chemical Engineering, Yosu National Fisheries College)
  • 김완영 (전북대학교 공업화학과) ;
  • 김윤섭 (전북대학교 공업화학과) ;
  • 육경창 (전북대학교 공업화학과) ;
  • 김형순 (전북대학교 공업화학과) ;
  • 이정용 (한국과학기술원 전자재료공학과) ;
  • 최상원 (여수수산대학 화학공학과)
  • Received : 1992.02.29
  • Accepted : 1992.07.04
  • Published : 1992.09.30
Download PDF
⟨ Previous Next ⟩

Abstract

The morphology and adhesion properties of rubber compounds containing resorcinol formaldehyde(RF) resin and hexamethoxymethylmelamine(HMMM) used in adhesion of rubber to brass-plated steel cord was investigated. The resins were spherical particles about $2000{\AA}$ diameter and distributed in rubber compounds homogeneously, and the cured compound with steel cord showed migration of resin to steel cord. Also, modulus was increased with increasing HMMM contents. The loss of adhesion between rubber and steel cord was likely to be at initial stages by thermal aging. Considering the physical properties, suability of adhesion layer and thermal aging property, optimum ratio of RF resin and HMMM was 1 : 0.9.

본 연구는 고무와 황동피복 코드간의 접착력 향상을 위하여 사용되는 resorcinol formaldehyde(RF) resin과 hexamethoxymethylmelamine(HMMM)이 고무 컴파운드내에서 나타내는 morphology와 접착특성에 대하여 고찰하였다. 가황후 resin은 구형의 형태로 시편 전체에 고르게 분포되어 있었고 그의 입경은 약 $2000{\AA}$정도였다. 코드와 함께 가황시킨 시편에서 코드 주위에 존재하는 resin함량이 감소한 것으로 보아 resin이 코드쪽으로 이동이 있었던 것으로 생각된다. 또한 모듈러스는 methylene donor인 HMMM의 양이 많을수록 증가하였으며, 접착층이 더 두껍게 형성되었다. 접착력은 열 노화에 의하여 상실되며 이는 대부분 초기에 발생함을 알 수 있었다. 접착컴파운드에서 가장 유리한 RF resin과 HMMM의 비는 물성, 접착층의 안정성, 열노화특성 등을 고려할 때 1 : 0.9이었다.