Abstract
NiCuZn ferrites were prepared by a solid-state reaction and sintered at $900^{\circ}C$ for 5 hours. Its properties were investigated by controlling the ferrite composition and processing. NiCuZn ferrite with a composition of ${(Ni_{0.2}Cu_{0.2}Zn_{0.6}O)}_{1.02}{(Fe_{2}O_{3})}_{0.98}$ was found to have the maximum initial permeability as a result of the variation of Cu content and the (Ni+Cu)/Zn ratio. Curie temperature($T_{c}$) of NiCuZn ferrite was decreased with the larger Cu content and increased with the larger Ni content. NiCuZn ferrites of ${(Ni_{0.2}Cu_{0.2}Zn_{0.6}O)}_{1-w}{(Fe_{2}O_{3})}_{1+w}$ composition milled for 20~80 hours had the maximum initial permeability at w=-0.015 and Curie temperature ($T_{c}$) was decreased with the increasing of $Fe_{2}O_{3}$ deficiency(w).
고상반응법에 의해 NiCuZn ferrite를 제조하였으며 소결온도 $900^{\circ}C$에서의 조성 및 공정변화에 따른 특성을 검토하였다. NiCuZn ferrite에서 Cu 치환 첨가량과 (Ni+Cu)/Zn의 조성비를 변화시킨 결과 ${(Ni_{0.2}Cu_{0.2}Zn_{0.6}O)}_{1.02}{(Fe_{2}O_{3})}_{0.98}$의 조성을 가질 때 초기투자율이 가장 높게 나타났다. NiCuZn ferrite의 Curie 온도 ($T_{c}$)는 Cu의 치환 첨가량이 증가함에 따라 점차 감소하였으며, Cu의 함량을 고정하고 Ni의 함량을 변화시킬 경우, (Ni+Cu)/Zn의 조성비가 증가할 수록 현저하게 증가하였다. ${(Ni_{0.2}Cu_{0.2}Zn_{0.6}O)}_{1-w}{(Fe_{2}O_{3})}_{1+w}$의 조성에서 분쇄시간을 20~80시간으로 변화시켰을 경우 $Fe_{2}O_{3}$ 결핍량(w)이 -0.015일 때 초기투자율이 가장 높았으며, Curie 온도 ($T_{c}$)는 $Fe_{2}O_{3}$ 결핍량(w)이 0에서 -0.025로 증가할 수록 점차 감소하였다.