The relation of structural transition and electrical property by deintercalation of Li-Carbon intercalation compounds (I) : For the formation of Li-GFDICs and Li-PCDICs

리튬-탄소층간화합물의 Deintercalation에 따른 구조변이와 전기적 성질과의 관계(I) : Li-GFDICs와 Li-PCDICs의 생성에 대하여

  • Oh, Won-Chun (Institute of Carbon Chemistry, Seoul National University of Education) ;
  • Baek, Dae-Jin (Department of Chemistry, Hanseo University) ;
  • Ko, Young-Shin (Institute of Carbon Chemistry, Seoul National University of Education)
  • 오원춘 (서울교육대학교 탄소화학연구소) ;
  • 백대진 (한서대학교 화학과) ;
  • 고영신 (서울교육대학교 탄소화학연구소)
  • Received : 1995.01.10
  • Published : 1995.06.25
Download PDF
⟨ Previous Next ⟩

Abstract

We have discussed on the structural transition and its effect on the electrical property of Li-GFDICs and Li-PCDICs occuring during the deintercalation process of Li-Graphite Fiber Intercalation Compounds(Li-GFICs) and Li-Petroleum Cokes Intercalation Compounds(Li-PCDICs) synthesized under pressure and temperature by spontaneous oxidation by air circulation. The analytical results were obtained by X-ray diffraction and electrical specific resistivity measurements. According to X-ray analysis, we have found that the major stage of Li-GFICs was stage 2 and those of Li-PCICs were stage 1 and stage 2, respectively. And from this results of the deintercalation process, we have found that the deintercalation process did not occur any more after 5th week of Li-GFDICs and after 3rd week of Li-PCDICs. According to the results of the electrical specific resistivity measurements, Li-GFDICs showed little variation to 3rd week and rising in the steady curve after 4th week, while Li-PCDICs showed a rising in the steady curve to 3rd week and a declining curve after 3rd week. Therefore from these results, we can consider that graphite fiber and petroleum cokes as a substrate can be also used as an anode material of battery because they have good intercalation-deintercalation reactivity with lithium.

가온 가압법으로 합성한 리튬-흑연섬유간화합물(Li-Graphite Fiber Intercalation Compounds, Li-GFICs)과 리튬-석유코크스층간화합물(Li-Petroleum Cokes Intercalation Compounds, Li-PCICs)을 공기 순환에 의하여 자발적으로 deintercalation시키고, 이 deintercalation의 분해 과정으로 나타나는 Li-GFDICs와 Li-PCICs의 구조를 전기적 성질에 미치는 영향에 대하여 논의하였다. 이에 대한 분석은 X-선 회절과 전기 비저항 측정에 의해 수행되었다. X-선 회절 분석에 의하면 Li-GFDICs의 경우 주로 2 stage가 형성되었고 Li-PCICs의 경우에는 1 stage와 2 stage가 주된 회절선으로 나타났다. 또한 deintercalatlon 반응 결과에 의하면 Li-GFDICs의 경우 5주 이후에, Li-GFDICs의 경우 3주 후에 deintercalation 반응이 각각 멈췄다. 전기 비저항 측정 결과에 의하면 Li-GFDICs의 경우 3주까지는 거의 변화가 없었고 그 후 완만한 상승곡선을 나타내었으며, Li-PCDICs의 경우에는 3주를 정점으로 하향곡선을 나타내었다. 따라서 본 연구결과에 의하면 기질로 사용된 흑연섬유와 석유 코크스의 경우 리튬의 원활한 intercalation-deintercalation 작용이 잘 이루어지므로 두 물질 모두 전지의 양극재로 사용될 수 있을 것으로 기대되어진다.