Study on the Development of Highly Efficient Compatibilizer for Polymer Alloys

고분자 알로이용 고효율 상용화제의 개발에 관한 연구

  • 조창기 (한양대학교 공과대학 섬유공학과)
  • Received : 1996.04.03
  • Accepted : 1996.06.17
  • Published : 1996.08.10
Download PDF
⟨ Previous Next ⟩

Abstract

Poly(alkyl acrylate-g-caprolactone) graft copolymers were prepared, and they were applied as compatibilizing agents for polycarbonate (PC) / poly(acrylonitrile-butadiene-styrene) (ABS) blends. The incompatible poly(alkyl acrylate) segment was incorporated into the graft copolymer in order to localize the copolymer at the PC/ABS interface. The blend containing 1 phr of the copolymer showed remarkable improvement in impact strength as well as in elongation at break. Impact improvement was more pronounced with a thinner test specimens of 1/8 inch thickness. Morphological study showed that the presence of the graft copolymer led to a smoother PC/ABS interface due to the interfacial enrichment of the graft copolymer.

폴리(알킬아크릴레이트-g-카프로락톤) 그라프트 공중합체를 합성하였으며, 이것을 폴리카보네이트(PC)/폴리(아크릴로니트릴-부타디엔-스티렌)(ABS) 블렌드의 상용화제로 사용하였다. PC나 ABS와 비상용성인 폴리 알킬아크릴 레이트 주사슬을 갖는 그라프트 공중합체를 사용하였으며 이것을 PC/ABS의 계면에 위치시키는 것을 목표로 하였다. 그라프트 공중합체를 1중량부 포함하는 블렌드물은 충격 강도는 물론 파단 인장 강도에서 아주 향상된 값을 보였으며, 1/8인치 시편에서의 충격 강도 향상이 두드러졌다. 전자현미경에 의한 형태학적인 분석 결과 그라프트 공중합체의 존재가 좀더 매끄러운 PC/ABS 계면을 형성하게 하는 것으로 나타났다.

Keywords

Acknowledgement

Supported by : 한국학술진흥재단

References

  1. Polymer Blends D. R. Paul
  2. Polymer Alloys and Blends L. A. Utracki
  3. Polymer Blends and Alloys M. J. Folkes;R. S. Hope
  4. Makromol. Chem., Makromol. Symp. v.16 L.Leibler
  5. Macromolecules v.15 J. Noolandi;K. M. Hong
  6. Macromolecules v.17 J. Noolandi;K. M. Hong
  7. Macromolecules v.25 K. H. Dai;E. J. Kramer;K. R. Shull
  8. Polymer v.33 S. Thomas;R. E. Prud'homme
  9. Macromolecules v.22 H. R. Brown
  10. Macromolecules v.26 C. Auschra;R. Stadler
  11. Macromolecules v.24 Ph. Dubois;R. Jerome;Ph. Teyssie
  12. Polymer v.34 L. Dong;R. Greco;G. Orsello
  13. Polymer Handbook(3rd ed.) J. Brandrup;E. H. Immergut
  14. Birt. Polym. J. v.19 G. C. Eastmond;J. M. Ming;M. Malinconico
  15. Polymer v.32 P. Sakellariou;G. C. Eastmond;I. S. Miles
  16. Polmer v.33 P. Sakellariou;G. C. Eastmond;I. S. Miles
  17. Polymer(Korea) v.19 K. S. Suh;D. S. Lee;C. G. Kang
  18. J. of Applied Polymer Sci. v.29 H. Surez;J. W. Barlow;D. R. Paul
  19. Polymer. Eng. and Sci. v.27 W. -Y. chiang;D. -S. Hwung
  20. Encyclopedia of Polymer Science and Engineering(2nd ed.) v.11 H. Mark