Abstract
The preparation of alumina sol for fine chemical field from kaolin-derived aluminum sulfate solution is performed. Noncrystalline AlO(OH) was prepared by dropping ammonia water into aluminum sufate solution with stirring. Acetetic acid was added to form the electrical double layers on the particle surface of the slurry, which resulted in a stable sol. The influence of the reaction temperature, reaction time, acetetic acid concentration on the preparation of alumina sol were investigated. Dispersed colloid particles of AlO(OH) were prepared at the reaction temperature of $50{\sim}90^{\circ}C$ and 1.6 A/C = 1.6 (molar ratio), regardless of the reaction time. Stable alumina sol having a particle size of about 5~10 nm was prepared in the range 1~5 vol% alumina content.
카올린에서 추출된 황산알루미늄 용액을 이용하여 정밀화학 분야에서 많은 이용이 기대되고 있는 알루미나 졸의 제조에 대하여 연구하였다. 교반을 하면서 황산알루미늄용액에 암모니아수를 첨가하여 비정질의 일수산화알루미늄(AlO(OH))를 제조하고, 제조된 입자의 표면에 전기이중층을 형성하기 위해서 초산($CH^3COOH$)을 투입하여 안정한 알루미나 졸을 제조하였다. 안정한 알루미나 졸의 제조에 미치는 반응온도, 반응시간, 초산의 농도 등의 영향을 조사하였다. 반응온도 $50{\sim}90^{\circ}C$, A/C(건조된 알루미나 량/첨가된 초산의 량) 1.6 (몰비)에서 안정한 졸의 합성이 가능하였으며, 반응시간에는 거의 영향을 받지않았다. 또한, 알루미나의 함량이 1~5vol%까지의 범위에서 안정한 졸이 제조되었고, 이때 졸의 입자크기는 약 5~10nm 정도이었다.