Abstract
We have studied on the magnetic properties of the specimen with additives Bi$_2$O$_3$and$V_2O_5$ that sintered at 900 $^{\circ}C$ for 4 hours for sybthesizing optimal Ni-Zn-Cu ferrite. Curie temperature rises from 240 $^{\circ}C$ to 270 $^{\circ}C$ as Ni contents increase. Magentic maximum induction$(B_m)$ increases from 2650 G to 3300 G, 3500 G in the specimens with $V_2O_5$ and Bi$_2$O$_3$resectively. On the contrary coercive force $(H_c)$ lowers to 2.05 Oe~1.05 Oe. Permeability all increase in the specimen with additives. In the specimen with additive Bi$_2$O$_3$, we have obtained the low relative loss factor of $6.3{\times}10^{-5}~7.84{\times}10^{-5}$ in the range of 1MHz due to increase of resistivity in grain boundary. In the specimen with additive $V_2O_5$ in spite of increase permeability relative loss factor increase of due to decrease of Q-value.
본 논문은 자기적 특성이 우수한 Ni-Zn-Cu ferrite를 얻기 위해 Bi2O3와 V2O5를 첨가하여 90$0^{\circ}C$에서 4시간 동안 소결한 후 각각의 시편에 대해서 물리적, 자기적 특성을 조사하였다. 큐리 온도는 Ni의 첨가량이 증가할수록 240~27$0^{\circ}C$까지 거의 직선적으로 증가하였다. 첨가제로 V2O5 와 Bi2O3를 사용한 경우 저온에서 소결을 가능하게 하여 최대 자속 밀도 Bm을 2650G에서 각각 3300G, 3500G로 높일수 있었으며 보자력은 2.05~1.05Oe까지 감소하였다. 첨가제로 V2O5와 Bi2O3를 사용한 경우 모두 투자율이 증가하였다. 상대 손실 계수는 Bi2O3를 첨가한 경우 입게의 비저항을 높여, 1 MHz의 주파수 대역에서 상대 손실 계수를 측정한 결과 6.3$\times$10-5~7.84$\times$10-5의 낮은 값을 얻었다. V2O5의 경우에는 투자율은 증가하였으나 Q값이 감소하여 상대 손실 계수가 증가하였다.