Field Emission Characteristics a-C:F:N Film Deposited by Inductively Coupled Plasma Chemical Vapor Deposition

Amorphous fluorocarbon (a-C:F) is of interest for low dielectric interlayer material, but in this work we applied this material to FED field emitter. N-doped a-C:F films were deposited by inductively coupled plasma chemical vapor deposition (ICPCVD). The Raman spectra were measured to study the film structure and inter-band optical absorption coefficients were measured using Perkin-Elmer UV-VIS-IR spectrophotometer and optical band gap was obtained using Tauc's plot. XPS spectrum and AFM image were investigated to study bond structure and surface morphology. Current-electric field(I-E) characteristic of the film was measured for the characterization of electron emission properties. The optimum doping concentration was found to be [N2]/[CF4]=9% in the gas phase. The turn-on field and the emission current density at $[N_2]/[CF_4]$=9% were found to be 7.34V/$\mu\textrm{m}$ and 16 $\mu\textrm{A}/\textrm{cm}^2$ at 12.8V/$\mu\textrm{m}$, respectively.