Properties of Wood-Based Board Prepared with Bed-Logs Decayed by Oak Mushroom(Lentinus edodes)

표고 폐골목으로 제조한 목질보드의 성질

To provide further information for reutilization of the bed-logs decayed by oak mushroom(Lentinus edodes), the properties of wood-based board prepared with mixed materials of normal wood and bed-logs were examined. Wood fibers in bed-logs showed different morphology from normal wood fibers, that is, shorter length and rough surface. Thickness swelling increased with increasing mixing ratio of bed-log. On the other hand, modulus of rupture(MOR) in bending strength decreased. In products, the visual surface of board prepared from higher mixing rate of bed-log chips was smooth. Consquently, it is considered that the optimum mixing rate of bed-log to normal wood is the range of 25-50% and the bed-log can be used for raw material of board instead of normal wood.

표고폐골목의 재활용을 목적으로 폐골목과 정상재의 칩을 일정비율로 혼합하여 얻은 목질보드의 성질을 조사, 검토하였다. 그 결과 폐골목의 목섬유는 정상재보다 다소 짧고 표면이 거철었으며 폐골목 변재부의 밀도는 정상재에 비해 상당히 낮았다. 파티클보드의 두께 팽윤율 및 파괴계수의 시험결과 폐골목을 25-50% 정도 혼합한 경우는 정상재와 비슷한 값을 나타냈다. 결론적으로 폐골목은 파티클보드의 재료로 사용될 수 있고 정상재와의 혼합비율은 25~50% 범위에서 조정되어야 할 것으로 생각되었다.