Synthesis of Two Dimensional Polymer Network

이차원 구조를 갖는 고분자의 합성

  • Shin, Jae Sup (Department of Chemistry, Chungbuk National University)
  • 신재섭 (충북대학교 자연과학대학 화학과)
  • Received : 1998.05.15
  • Accepted : 1998.06.08
  • Published : 1998.10.10
Download PDF
⟨ Previous Next ⟩

Abstract

Cholesterol-containing surfactant was synthesized, and it was sonicated with monomer [tetradeca(ethylene glycol) diacrylate] in water to from a vesicle solution. This vesicle solution was dried to construct a membrane which had a molecular multilayer structure. The monomer which stay in this membrane was polymerized with photoinitiation, and then surfactant was extracted by organic solvent. The physical properties of the two dimensional polymer network were measured, and these physical properties are tensile strength, elongation, and swelling.

콜레스테롤을 갖는 계면활성제를 합성하고, 이 계면활성제를 단량체[tetradeca(ethylene glycol) diacrylate]와 함께 물 속에서 음파 파쇄하여 vesicle 용액을 형성한 다음, 이 용액내의 물을 증발시켜, 분자들이 규칙적으로 배열된 분자 다층 구조를 갖는 막을 합성하였다. 이 막에 들어 있는 단량체들을 광중합하여, 고분자가 계면활성제들의 층과 층 사이에 들어 있는 분자 다층 구조를 합성하였다. 중합이 끝난 후 유기 용매를 사용하여 계면활성제를 추출하여 이차원적인 구조를 갖는 얇은 박막 층으로 이루어진 고분자 막을 합성하였다. 형성된 이차원 구조를 갖는 고분자 막의 물성을 측정하였는데, 막의 물성으로는 인장 강도, 신장율, 팽윤 등을 측정하였다.

Keywords

Acknowledgement

Supported by : 교육부

References

  1. Acc. Chem. Res. v.13 J. H. Fendler
  2. Membrane Mimetic Chemistry J. H. Fendler
  3. J. Am. Chem. Soc. v.103 M. S. Tunuli;J. H. Fendler
  4. J. Am. Chem. Soc. v.106 Y. M. Tricot;J. H. Fendler
  5. J. Chem. Soc. Chem. Commun. R. A. Moss;J. S. Shin
  6. J. Am. Chem. Soc. v.109 R. A. Moss;S. Bhattacharys;P. Scrimin;S. Swarup
  7. J. Am. Chem. Soc. v.114 R. A. Moss;Y. Okumura
  8. J. Kor. Ind. Eng. Chem. v.2 J. S. Shin
  9. Polymer(Korea) v.15 I. Cho;J. S. Shin
  10. J. Kor. Ind. Eng. Chem. v.3 D. H. Bae;K. S. Kim;J. S. Shin
  11. Macromolecules v.17 I. Cho;K. C. Chang
  12. Macromolecules v.21 I. Cho;K. C. Chang
  13. Chem. Lett. I. Cho;J. G. Park
  14. Polymer Bulletin v.24 I. Cho;Y. W. Kim
  15. J. Kor. Ind. Eng. Chem. v.3 I. Cho;S. H. Kim;J. S. Shin
  16. Polymer (Korea) v.18 I. Cho;S. J. Jeong;J. S. Shin
  17. Polymer (Korea) v.19 J. S. Shin
  18. J. Kor. Ind. Eng. Chem. v.7 J. S. Shin
  19. Chemworld v.33 H. Lee
  20. Chemworld v.34 J. W. Park
  21. Polymer Sci. Tech. v.5 H. Lee