(Dept. of Polymer Engineering, The University of Suwon)
;
Hot melt adhesive which is solventless type has been widely used due to the possibility of automated adhesion process. The main purpose of this study is the development of polyamide based hot melt adhesive to improve the property of conventional ethylene-vinyl acetate hot melt adhesive, which has an inherent problem against heat resistance. In this study, it was found that the terpolymers of nylon 6, nylon 66, and nylon 12(CM831, 843P types) instead of nylon homopolymer were suitable base resins for hot melt adhesive, since the disruption of regularity in the polymer chains reduced the crystallinity, resulting in lower melting point and melt viscosity. According to the results, the optimum adhesion property could be obtained by the using 75/25~50/50 weight radio of CM831/843P resin as a base resin. Terpene resin was used as tackifier to improve adhesion and wetting properties. The best result can be obtained with the 10 wt.% addition of terpene resin. The terpene resin acted as proper tackifier in this system which decreased the melt temperature and viscosity, but increased the mechanical strength of adhesive itself. Also, the rheological property of the adhesive changed from typical non-Newtonian behavior to Newtonian behavior as terpene resin was added.
핫멜트 접착제는 최근 대두되고 있는 환경적인 요구사항들을 충족시킬 수 있는 무용제형이고 접착공정의 자동화가 가능하기 때문에 널리 사용되고 있다. 본 연구에서는 핫멜트 접착제의 기본 수지로서 폴리아미드 단일중합체 대신 나일론 6, 나일론 66, 나일론 12로 이루어진 CM831(랜덤중합체)과 843P(블록중합체) 형의 두 종류 수지를 사용하여 핫멜트 접착제를 제조하였다. 결과에 의하면 접착제 자체 강인성을 크게 손상하지 않는 범위에서 가능한 한 낮은 용융점도를 갖는 조건은 CM831/843P 수지 블랜딩 비율이 약 75/25~50/50임을 알 수 있었다. 접착성 향상과 더불어 피착제와의 젖음 특성 향상을 위해 점착부여 수지로 테르펜 수지를 사용하였다. 테르펜 수지는 약 10 wt.% 첨가되었을때 현 시스템의 용융온도와 용융점도를 감소시키고, 접착제 자체 강인성은 증가시키는 접착제 측면에서 바람직한 결과를 나타냈다. 또한 접착제의 유변학적 특성도 전형적인 비뉴턴 거동으로부터 테르펜수지 첨가로 인해 뉴턴 거동에 가까워졌다.
Supported by : 한국과학재단