Abstract
Frequency and temperature dependence of magnetic loss has been investigated in Mn-Zn ferrites containing the sesistive temary compounds of $SiO_2-CaO-V_2O_5$. The Mn-Zn ferrite with the composition of $MnO:ZnO:Fe_2O_3=36:11:53$(by mol %) are prepared by self-propagating high-temperature synthesis. From the results of frequency dependence of core loss, it has been found that the hysteresis loss is dominant at low frequency and the eddy current loss becomes more dominant as the frequency increases. With the addition of resistive compound, the frequency dependence of core loss, it has been found that the hysteresis loss is dominant at low frequency and the eddy current loss becomes more dominant as the frequency increases. With the addition of resistive compound, the frequency region where the hysteresis loss is dominant becomes wide. The core-loss minimum occurs at about 4$0^{\circ}C$ in the specimens with the additive because of the reduction in eddy current loss.
SiO2-CaO-V2O5 3원계 첨가물을 함유한 Mn-Zn 페라이트 저손실의 주파수 및 온도 의존성에 대해 조사하고 주된 자기손실기구에 대해 고찰하였다. 연쇄고온합성법에 의해 MnO:ZnO:FeO=36:11:53mol% 조성의 페라이트를 제조하였다. 자기손실의 주파수 의존 결과로부터 저주파에서는 자기이력손실이 고주파에서는 와전류손실이 지배적임을 제시하였고, 고저항 첨가제에 의해 비저항이증가할수록 자기이력손실이 감소하였다. 순수 Mn-Zn 페라이트의 경우 자기 손실은 온도 증가에 따라 증가하였으나, 입계저항제가 첨가된 시편의 경우 와전류손실의 감소로 약 4$0^{\circ}C$에 서 자기손실의 최소치가 나타났다.