Abstract
We have investigated some crystallographic, magnetic, and transport properties of the first colossal magnetoresistive compounds $La_{1-x}Ba_{x}MnO_3(0\leq\chi\leq$1)$(5\;K\leqT\leq360K,-5T\leqH\leq5T$ and resistivity $(100K\leqT\leq350K$measurements. $La_{1-x}Ba_{x}MnO_3$ were found to be ferromagnetic for all x.The $La_{1-x}Ba_{x}MnO_3$were found to be insulating for x< 0.2, metallic for 0.20.5. The magnitude of saturation magnetization (Ms) increased until x=1/8 and had theoretical maximum Ms for 0.13$\sfrac{3}{8}$ and had a constant value of 335~340 K for x>$\sfrac{3}{8}$. For $x\geq0.5$ the $La_{1-x}Ba_{x}MnO_3$ samples showed a percolation-type conduction behavior and enhanced low field magnetoresistance caused by simultaneous occurrence of the chemical/magnetic phase separation.
최초의 상온 초거대 자기저항(colossal magnetoresistance)효과 물질인 망간 산화물$La_{1-x}Ba_{x}MnO_3(0\leq\chi\leq$1) 에 대한 결정학적, 자기적, 전기적 성질들을 온도 및 자기장의 함수$5\;K\leqT\leq360\;K,\;-7\;T\leqH\leq7\;T)$로 정밀 조사하였다. $La_{1-x}Ba_{x}MnO_3$는 x<1/2 일 때는 x에 의존하는 구조를 가진 단일상(single phase)의 강자성, $x\geq1/2$ 일 때는 화학적, 자기적 상분리에 의한 강자성과 비강자성 복합상(multi phase)을 가지는 것으로 나타났다. 강자성 전이 온도(Tc)는 x=1/3이 될 때까지 꾸준히 증가하였고 x＞1/3 일 때 일정한 값 Tc(340 K)을 가졌다. 또 포화 자화값(Ms)은 x=1/8이 될 때까지 증가하였고 $1/8\leqx<1/2$에서는 이론적인 최대값을 가지고$x\geq1/2$ 에서는 자기적 상분리에 의해 감소하였다. 또 $La_{1-x}Ba_{x}MnO_3$는 $1/4\leqx<1/2$에서 금속성을 가졌다. 특히 $x\geq1/2$인 시료는 화학적, 자기적 상분리로 인하여 스미기 형태(percolation type)의 저항 온도 의존성 및 큰 저자기장 자기 저항 효과를 보였다.