Magnetic Properties of Sintered Fe Cores Containing Stainless Steel-making Dusts

스테인레스 제강 분진을 함유한 순철 소결코아의 자기특성

  • 김상원 (포항산업과학연구원 재료공정연구센터 금속코팅재료연구팀)
  • Published : 2001.06.01

Abstract

Effect of sintering temperature and dusts content on sintered density ($\rho$) and magnetic properties were evaluated. Cores sintered at 1350 $^{\circ}C$ for 1 hour with the Fe powders containing up to 10 wt.% dusts showed a good AC/DC properties. For example, the DC magnetic properties of magnetic induction (B$_{15}$), coercive force (H$_{c}$) and permeability ($\mu$$_{max}$) of cores containing 10 wt.% dusts were ranging over 9.8~ 10.9 kG, 2.2-2.3 Oe and 1950~2050, respectively. These magnetic properties are equivalent to those of competitor's (i.e, Ancorsteel produced by Hoganas). The cores obtained from the present work are expected to apply for high-performance soft magnetic components such as automotive and DC motor.

순털 코아의 소결밀도와 자기특성에 미치는 분진의 첨가량과 소결온도의 영향을 조사하였다. 1350 $^{\circ}C$에서 1시간동안 소결한 경우 최고의 자기특성을 나타내었으며, 분진의 첨가량이 증가할수록 자기특성은 열악해지나 10 wt.%까지는 양호하였다. 한 예로 10 Wt.%의 분진 첨가로 얻어진 직류자기특성은, 자속밀도(B$_{15}$), 보자력(H$_{c}$)과 최대투자율($\mu$$_{max}$)이 각각 9.8~10.9 kG, 2.2~2.3 Oe, 1950~2050로 나타났다. 이 값은 Hoganas사에서 제조된 순철 분말(Ancorsteel)의 자기특성과 동등한 수준이며, 본 연구에서 얻어진 우수한 특성의 소결코아는 자동차, DC 모터의 고정자 등에 활용이 기대된다.

Keywords

References

  1. 日本公開特許公報 昭
  2. 日本公開特許公報 昭
  3. 日本公開特許公報 昭
  4. Metal Powder Industries Federation Soft Magnetism C.Lall
  5. 연구보고서 STS공장 발생분진의 분리집진기술 김상원;양충진;박언병
  6. 粉末冶金學 李鐘南;文仁炯
  7. 한국자기학회지 v.6 no.6 김상원;양충진
  8. Metal Powder Industries Federation Soft Magnetism C.Lall
  9. Digest of Soft Magnetic Materials 96 Gorham/Intertech Consulting K.S.Narsimhan