Improvement of Magnetic Properties of Nd-Fe-B Type Sintered Magnet

Nd-Fe-B계 소결자석의 자기적특성 향상 연구

  • 김윤배 (한국과학기술연구원 금속공정연구센터) ;
  • 정우상 (한국과학기술연구원 금속공정연구센터) ;
  • 정원용 (한국과학기술연구원 금속공정연구센터)
  • Published : 2002.04.01
Download PDF
⟨ Previous Next ⟩

Abstract

In order to increase the magnetic properties of a Nd-Fe-B sintered magnet, the general factors including particle size and its distribution, volume fraction of Nd$_2$Fe$_{14}$B phase, degree of alignment of Nd$_2$Fe$_{14}$B grain, oxygen content and grain size etc. should be optimized by controlling the composition of Nd-Fe-B alloy as well as the manufacturing process. In this study, fabrication of the Nd-Fe-B sintered magnet was carried out in a laboratory scale by controlling the composition of Nd-Fe-B alloy and the manufacturing process. The optimum milling condition was found by investigating the milling media, milling time and ball size. The addition of FeGa was effective to increase the coercivity of the Nd-Fe-B sintered magnet. A remanence of 14.4 kG, a coercivity of 9.4 kOe and a maximum energy product of 47 MGOe were obtained from the sintered magnet.

Nd-Fe-B계 소결자석의 특성을 향상시키기 위해서는 Nd-Fe-B계 합금의 조성 및 제조공정을 조절하여 자성분말의 입도 및 입도분포, 강자성상인 N $d_2$F $e_{14}$B상의 분율, 자성분말의 배향도, 산소 함량, grain size 등과 같은 factor들을 최적화 하여야 한다. 본 연구에서는 실험실 규모로 Nd-Fe-B계 합금 조성 및 공정 조절을 통하여 Nd-Fe-B계 소결자석을 제조하는 연구를 수행하였으며, 분쇄매체 분쇄시간 및 ball size에 따른 Nd-Fe-B계 소결자석의 자기적특성을 분석하여 최적의 분쇄조건을 조사하였다. 또한 분쇄공정 중 FeGa합금을 첨가하여 잔류자속밀도의 감소없이 Nd-Fe-B계 소결자석의 보자력을 향상시킬 수 있었다. 이와 같은 분쇄 조건의 연구, FeGa 합금에 의한 보자력 향상, 건식분쇄 방법 및 powder blending 공정을 적용하여 잔류자속밀도( $B_{r}$,) : 14.4kG, 보자력($_{i}$ $H_{c}$) : 9.4kOe, 최대자기에너지적((BH)$_{\max}$) : 47 MGOe의 자기적 특성을 갖는 Nd-Fe-B계 소결자석을 제조하였다.

Keywords

References

  1. IEEE Trans. Mag v.36 no.5 Y. Kaneko https://doi.org/10.1109/20.908767
  2. J. Mater. Eng. and Perf v.1 M. Honshima;K. Ohashi
  3. USP v.5 K. Takebuchi;S. Fujito;S. Hashimoto;K. Yajima
  4. J. Appl. Phys. v.55 J. J. Croat;J. F. Herbst;P. W. Lee;P. E. Pinkerton https://doi.org/10.1063/1.333571
  5. Prog. Phys. v.54 K. H. Buchow https://doi.org/10.1088/0034-4885/54/9/001
  6. IEEE Trans. Magn. v.25 V. Panchanathan;J. J. Croat https://doi.org/10.1109/20.42538
  7. IEEE Trans. Magn v.26 S. X. Zhou;P. Johansson;S. J. Savage;L. Y. Cui https://doi.org/10.1109/20.104510
  8. J. Magn. Magn. Mater. v.157-158 H.A. Davies https://doi.org/10.1016/0304-8853(95)01271-0
  9. J. Appl. Phys. v.64 Y. Nozawa;K. Iwasaki;S. Tanigawa;M. Tokunage;H. Harada https://doi.org/10.1063/1.342394
  10. J. Appl. Phys v.83 T. Saito;M. Fujita;T. Kuji;K. Fukuoka;Y. Syono https://doi.org/10.1063/1.367522
  11. J. Appl. Phys. v.73 S. Hirosawa;H. Kanekjyo;M. Uehara https://doi.org/10.1063/1.352589
  12. J. Magn. Magn. Mater. v.157-158 J. F. Liu;H. A. Davies https://doi.org/10.1016/0304-8853(95)01051-3
  13. J. Alloys Compd v.193 R. Nakayama;T. Takeshita https://doi.org/10.1016/0925-8388(93)90364-S
  14. IEEE Trans. Magn v.23 M. Endoh.;M. Tokunaga;H. Harada https://doi.org/10.1109/TMAG.1987.1065291
  15. IEEE Trans. Magn. v.23 M. Tokunage;H. Kogure;M. Endoh;H. Harada https://doi.org/10.1109/TMAG.1987.1065287
  16. IEEE Trans. Magn. v.25 M. Tokunaga;Y. Nazawa;K. Iwasaki;M. Endoh;S. Tanigawa;H. Harada https://doi.org/10.1109/20.42365
  17. IEEE Trans. Magn. v.25 J. Hu.;Z. Wang;Y. Wang;J. Zhao;X. Rao;N. Zhang https://doi.org/10.1109/20.42324
  18. IEEE Trans. Magn. v.26 J. Fidler;C. Groiss;M. Tokunaga https://doi.org/10.1109/20.104917
  19. J. Magn. Magn. Mater v.83 M. Leonowicz https://doi.org/10.1016/0304-8853(90)90489-D
  20. J. Appl. Phys. v.71 B. Grieb.;C. Pithan;E.-Th. Henig;G. Petzow
  21. Solid State Commun v.72 C. G. Quan;Y. Z. Wang;L. Yin;J. G. Zhao https://doi.org/10.1016/0038-1098(89)90435-3
  22. IEEE Trans. Magn v.29 J. Bernardi;J. Fidler;M. Seeger;H. Kronmuller https://doi.org/10.1109/20.281024
  23. J. Appl. Phys v.83 T. Saito;M. Fujita;T. Kuji;K. Fukuoka;Y. Syono https://doi.org/10.1063/1.367522