Structural and Magnetic Properties of Fe-Si-C Alloys with Processing Times

Fe-Si-C 합금의 합금화 과정에 따른 구조 및 자기적 특성 변화 연구

  • 유용구 (한국전자통신연구원 반도체·원천연구소) ;
  • 김태엽 (한국전자통신연구원 반도체·원천연구소) ;
  • 김약연 (한국전자통신연구원 반도체·원천연구소) ;
  • 한기평 (한국전자통신연구원 반도체·원천연구소) ;
  • 유성초 (충북대학교 물리학과) ;
  • 양동석 (충북대학교 과학교육과) ;
  • Published : 2002.10.01
Download PDF
⟨ Previous Next ⟩

Abstract

Fe-Si-C alloy system has been made by mechancial alloying process. The structural and magnetic properties were analysed as a function of processing times. The structural properties were investigated by X-ray diffraction and EXAFS experiments. The magnetic properties were measured by vibrating sample magnetometer and M ssbauer spectroscopy. As processing time increases, Si and C atoms diffuse into a ${\alpha}$-Fe structure and then bcc solid solution is formed after 12 hours of the processing time. The magnetization and the hyper fine field decreased steeply up to 4 hours and then it changed slowly. After 12 hours of the processing time, it almost saturated. These results were agreed with the structural variation.

기계적 합금화 방법을 통하여 Fe-Si-C계 합금을 제조하였으며, 합금화 과정에 따른 구조 및 자기적 특성을 분석하였다 구조적 특성의 분석은 X-선 회절 실험과 EXAFS(extended X-ray absorption fine structure)실험을 통하여 수행하였고, 자기적 특성은 시료진동형자력계와 M ssbauer 분광법으로 연구하였다. 합금화 시간이 증가함에 따라 Si, C 원자들은 Fe 구조 속으로 확산되었으며, 12시간 이후로는 과포화된 bcc 고용체를 형성하였다. 합금화 시간에 따른 포화 자화값 및 초미세 자기장은 4시간까지 급격한 감소를 나타내었으며, 그 이후로는 완만한 감소를 나타내었고, 12시간 이후로는 변화가 적음을 나타내었다. 이러한 변화는 구조 특성 분석 결과와 일치하였다.

Keywords

References

  1. J. Ding, Y. Li, L. F. Chen, C. R. Deng, Y. Shi, Y. S. Chow, T. B. Gang, J. Alloys & Compounds, 314, 262(2001) https://doi.org/10.1016/S0925-8388(00)01234-2
  2. K. Oka, N. Yano, S. Furukawa, I. Ogasawara, J. Yamasaki, F. B. Humphrey, IEEE Trans. Magn., 31(6), 3997(1995) https://doi.org/10.1109/20.489842
  3. N. Randrianantoandro, E. GaHet, J. Mira, J. M. Grenech$'{e}$, Solid State Comm., 111, 323(1999) https://doi.org/10.1016/S0038-1098(99)00209-4
  4. M. Pekala, M. Jachimowicz, V. I. Padeeva, H. Matyja, A. Gra-bias, J. Non-Cryst. Solids, 287, 380(2001) https://doi.org/10.1016/S0022-3093(01)00602-0
  5. C. C. Koch, J. D. Whktenberger, Intermetallics, 4, 339(1996) https://doi.org/10.1016/0966-9795(96)00001-5
  6. A. R. Yavah. P. J. Desre, T. Benameur, Phys. Rev. Lett., 68(14), 2235(1992) https://doi.org/10.1103/PhysRevLett.68.2235
  7. Y. G. Yoo, S. -C. Yu, W. T. Kim, EEE Trans. Magn., 31(6), 3769(1995) https://doi.org/10.1109/20.489766
  8. Nurul TauSqu Rochman, K. Kawamoto, H. Sueyoshi, Y. Naka-mura, T. Nishida, J. Mat. Proc. Tech., 89-90, 367(1999)
  9. G. K. Williamson, W. H. Hall, Acta Met., 1, 22(1953) https://doi.org/10.1016/0001-6160(53)90006-6
  10. D. C. Koningsberger, R. Piins, eds. X-ray Absorption. Pnnci-pIes, Applications, Techniques of EXAFS, SEXAFS and XANES, Wiley, New York (1988)
  11. E. A. Stem, M. Newville, B. Ravel, Y. Yacoby, D. Haskel, Physica B, 208&209, 117(1995)
  12. D.-S. Yang, Y.-G. Yoo, S.-C. Yu, J. Phys. Soc. Jap., 71(2), 487 (2002) https://doi.org/10.1143/JPSJ.71.487
  13. G. Le Ca$\ddot{a}$r, P. Delcroix, T. D. Shen, B. Malaman, Phys. Rev. B54(18), 12775(1996) https://doi.org/10.1103/PhysRevB.54.12775
  14. J. M. Greneche, J. Non-Cryst. Solids, 287, 37(2001) https://doi.org/10.1016/S0022-3093(01)00634-2
  15. H. Ino, M. Kincho, K. Oda, K. Tokumitsu, Mat. Sci. & Eng., A312, 262(2001) https://doi.org/10.1016/S0921-5093(00)01868-2
  16. Tie-Jun Zhou, Z. Yu, Y.W. Du, J. Magn. & Magn. Mater., 202, 354(1999) https://doi.org/10.1016/S0304-8853(99)00384-4