Effects of Intra-particle Composition on the Adhesive Properties and Water Dispersity of Water Dispersible Acrylic Emulsion Pressure Sensitive Adhesive

입자 내 조성 변화가 수분산성 아크릴 에멀젼 점착제의 점착 물성과 수분산성에 미치는 영향

  • Seo, In Seon (Materials Research Center for Information Display, Kyung Hee University) ;
  • Lee, Myung Cheon (Department of Chemical and Biochemical Engineering, Dongguk University)
  • 서인선 (경희대학교 영상정보소재기술연구센터) ;
  • 이명천 (동국대학교 생명화학공학과)
  • Received : 2007.04.18
  • Accepted : 2007.09.10
  • Published : 2007.10.10
Download PDF
⟨ Previous Next ⟩

Abstract

The effects of intra-particle composition on the adhesive properties and water dispersity of acrylic emulsion type pressure sensitive adhesives (PSAs) were investigated. In the case of PSA having uniform intra-particle composition, the higher holding strength made the water dispersity lower. By changing the intra-particle composition in hard core/soft shell type, however, it was possible to get PSAs showing both high holding strength and water dispersity. When the weight ratio of MAA/AA is 4/1, high holding strength, but low initial tack and very low water dispersity were observed in both cases of higher contents of (AA+MAA) in core and shell area. When the weight ratio of MAA/AA is 1/4, however, higher water dispersity and lower holding strength were indicated in the case of higher contents of (AA+MAA) in shell area.

수분산성 점착제의 점착 물성과 수분산성에 미치는 입자 내 조성의 영향을 알아보기 위하여 다양한 입자 내 조성을 갖는 아크릴계 에멀젼형 점착제를 제조하여 각각의 점착 물성과 수분산성을 조사하였다. 입자 내 단일 조성을 갖는 경우 유지력과 수분산성을 동시에 만족시키기 어려웠으나 입자 내 조성을 hard core/soft shell 형태를 갖게 함으로써 수분산성은 적게 희생하고 유지력을 높일 수 있었다. 또한 메타크릴산/아크릴산(MAA/AA)의 중량비가 4/1인 경우에는 친수성 물질인(AA+MAA) 함량이 core로 갈수록 많은 경우와 shell로 갈수록 많은 경우 모두 유지력은 크게 상승했으나 초기점착력은 크게 낮아졌으며 수분산성은 거의 관찰되지 않았다. 그러나 MAA/AA 중량비가 1/4인 경우는 shell 부분에 (AA+MAA) 함량이 많은 경우에 수분산성이 더 컸으나 유지력은 상대적으로 적게 나타났다.

Keywords

References

  1. M. C. Lee, M. C. Park, I. S. Seo, Polymer Science and Technology, 11, 450 (2000) https://doi.org/10.1002/1099-1581(200008/12)11:8/12<450::AID-PAT991>3.0.CO;2-7
  2. S. D. Tobing and A. Klelin, J. Appl. Polym. Sci., 79, 2230 (2001) https://doi.org/10.1002/1097-4628(20010321)79:12<2230::AID-APP1030>3.0.CO;2-2
  3. J. Garrett, P. A. Lovell, A. J. Shea, and D. R. Viney, Macromol. Symp., 151, 487 (2000)
  4. C. Laureau, M. Vicente, M. J. Barandiaran, J. R. Leiza, and J. M. Asua, J. Appl. Polym. Sci., 81, 1258 (2001) https://doi.org/10.1002/app.1548
  5. Y. S. Park and S. G. Choi, J. Korean Ind. Eng. Chem., 12, 186 (2001)
  6. K. E. Min, H. G. Kim, K. Y. Choi, and K. H. Kwak, J. Appl. Polym. Sci., 74, 91 (1999)
  7. M. C. Park, I. S. Seo, M. C. Lee, H. S. Shin, and J. C. Lim, Polymer(Korea), 23, 625 (1999)
  8. Y. O. Seo and S. D. Seul, J. Korean Ind. Eng. Chem., 11, 335 (2000)
  9. J. Tang, V. L. Dimonie, E. S. Daniels, A. Klein, and M. S. El-Aasser, J. Appl. Polym. Sci., 77, 644 (2000)
  10. A. M. D. Santos, T. F. Mckenna, and J. Guillot, J. Appl. Polym. Sci., 65, 2343 (1997)
  11. C. S. Chern, C. F. Huang, and C. L. Wang, J. Disper. Sci. Technol., 19, 1 (1998)
  12. S.-C. Hsu, Y.-L. Liao, C.-F. Lee, and W.-Y. Chiu, J. Appl. Polym. Sci., 74, 3111 (1999)
  13. M. Slawinski, M. A. J. Schellekens, J. Meuldijk, A. M. Van Herk, and A. L. German, J. Appl. Polym. Sci., 76, 1186 (2000) https://doi.org/10.1002/(SICI)1097-4628(20000516)76:7<1186::AID-APP22>3.0.CO;2-N
  14. D.-Y. Lee and J.-H. Kim, J. Appl. Polym. Sci., 69, 543 (1998)
  15. J. W. Nicholson, Pigment & Resin technol., 26, 161 (1997)
  16. G. L. Shoaf and G. W. Poehlein, Ind. Eng. Chem. Res., 29, 1701 (1990) https://doi.org/10.1021/ie00104a020