Characterization of Activated Carbon from Wood by ZnCl2

염화아연(ZnCl2) 부활법에 의해 제조한 목재 활성탄의 특성

  • Kwon, Gu-Joong (Department of wood science and engineering, College of Forest and Environmental Sciences, Kangwon National University) ;
  • Kwon, Sung-Min (Department of wood science and engineering, College of Forest and Environmental Sciences, Kangwon National University) ;
  • Kim, Nam-Hun (Department of wood science and engineering, College of Forest and Environmental Sciences, Kangwon National University)
  • 권구중 (강원대학교 산림환경과학대학 임산공학과) ;
  • 권성민 (강원대학교 산림환경과학대학 임산공학과) ;
  • 김남훈 (강원대학교 산림환경과학대학 임산공학과)
  • Published : 2007.08.31
Download PDF
⟨ Previous Next ⟩

Abstract

The effect of ratio between chemical activating agent and raw material in the preparation of activated carbons from wood has been studied. Pinus koraiensis wood and zinc chloride ($ZnCl_2$) were used for materials in this study. Mixtures of wood and zinc chloride were heated under nitrogen flow in the temperature ranging from room-temperature to $600^{\circ}C$ for 1 hr using thermogravimetric technique. During heat treatment, activated carbons with various pore size and specific surface properties were obtained. The maximum BET surface area and total pore volume were $1468m^2/g$ and 1.74 cc/g, respectively, at the mixture ratio of 1 (wood powder) to 5 ($ZnCl_2$). It can be concluded that the differences in the properties of the activated carbons were related significantly with the ratio of chemical activating regent.

본 연구는 염화아연을 이용한 화학약품 부활법으로 잣나무재 활성탄을 제조하기 위해 원료에 대한 화학약품부활제 비율의 영향을 검토하였다. 염화아연과 혼합한 목분은 질소분위기에서 상온에서 $600^{\circ}C$까지 1시간 열처리하여 중량변화를 측정하였다. 이 처리과정에 있어 활성탄 내부에 다양한 공극크기 분포와 표면특성이 확인되었다. 즉, 최대 BET 표면적과 총 공극체적은 목분에 대하여 염화아연의 비율이 5배인 경우였으며, 각각 그 값은 $1468m^2/g$와 1.74 cc/g이었다. 결론적으로 활성탄 제조시 화학약품부활제의 비율에 의해 활성탄의 특성이 뚜렷하게 차이가 나타나는 것이 확인되었다.