Production properties of pyrolytic matter of PP and PS plastics in n low temperature pyrolysis condition

저온 열분해조건에서 PP 및 PS계 플라스틱의 열분해물 생성특성 연구

Thermal degradation characteristics of polypropylene and polystyrene have been studied in the thermogravimetric(TG) reactor and batch-type microreactor. The dynamic thermogravimetric curve of TG provided a valuable information about pyrolysis temperature. It was found that PS was thermally degraded at lower temperature of $30{\sim}50^{\circ}C$ than PP. It was found that the yield and molecular weight of liquid product in the microreactor were decreased with the increase of reaction temperature and time in the case of PP. The production of styrene monomer was significantly increased by the promotion of depolymerization with the increase of temperature and time. The chain-end scission rate parameters were determined to be 50.0 kcal/mole of PP, 45.2 kcal/mole of PS by the Arrhenius plot.

열중량반응기와 회분식 미분형반응기를 이용하여 Polypropylene(PP)과 Polystyrene(PS)의 열분해특성을 연구하였다. 열중량반응기로부터 얻은 동적 특성곡선은 열분해온도에 대한 만족할 만한 정보를 제공해 주었으며, PS가 PP보다 $30{\sim}50^{\circ}C$ 낮은 온도에서 열분해가 일어남을 알 수 있었다. 미분반응기에서 PP의 경우 열분해 온도와 시간이 증가할수록 액상 생성물의 수율과 분자량분포는 전체적으로 감소하는 경향을 보였다. PS의 경우 반응온도와 시간이 증가할수록 해중합이 촉진되어 styrene monomer의 생성이 두드러졌다. 열분해반응에서 말단절단의 속도계수인 활성화에너지 값은 PP의 경우 50.0 kcal/mole, PS의 경우 45.2 kcal/mole이었다.