Electromagnetic Wave Absorption Properties of NiCuZn Ferrite

NiCuZn 페라이트의 전자파 흡수특성

  • Park, Chan-Kyu (Department of Chemical Engineering, Dong-A University) ;
  • Kim, Ki-Tae (Department of Chemical Engineering, Dong-A University) ;
  • Chang, Sang-Mok (Department of Chemical Engineering, Dong-A University) ;
  • Lee, Sang-Rok (Department of Chemical Engineering, Dong-A University)
  • 박찬규 (동아대학교 공과대학 화학공학과) ;
  • 김기태 (동아대학교 공과대학 화학공학과) ;
  • 장상목 (동아대학교 공과대학 화학공학과) ;
  • 이상록 (동아대학교 공과대학 화학공학과)
  • Received : 2009.05.11
  • Accepted : 2009.07.01
  • Published : 2009.10.10
Download PDF
⟨ Previous Next ⟩

Abstract

NiCuZn Ferrites, known as preventing EMI/EMC, were prepared and their properties were investigated based on the chemical composition ratio, sintering temperature, and mean particle size. The NiCuZn ferrite made of $Fe_2O_3$ 49.0 mol%, NiO 9.0 mol%, CuO 8.0 mol%, ZnO 34.0 mol% could be applied at the largest range of electromagnetic wave. The optimal calcination and sintering temperature were $900^{\circ}C$ and $1080^{\circ}C$, respectively. The electromagnetic wave loss capacity of its mean particle size $1.12{\mu}m$ was superior to others examined.

전자파 흡수용 재료로서 NiCuZn 페라이트의 제조조건 중 구성성분비, 소결온도, 평균입자 크기에 대하여 자기적 특성을 검토하였다. 전자파 흡수용 재료로서의 NiCuZn 페라이트가 가장 넓은 주파수 대역에 적용될 수 있는 화학적 조성비는 $Fe_2O_3$ 49.0 mol%, NiO 9.0 mol%, CuO 8.0 mol%, ZnO 34.0 mol%이다. 이 화학조성에서 배합한 원료를 $900^{\circ}C$에서 하소하여 제조한 페라이트를 성형하여 $1080^{\circ}C$에서 소결시킨 페라이트 상태를 관찰한 결과 결정립 $5{\sim}10{\mu}m$로서 최적의 상태를 보였다. 평균입자크기가 $1.12{\mu}m$의 경우 가장 우수한 손실탄젠트 및 전자파 흡수특성을 나타내었다.

Keywords

Acknowledgement

Supported by : 동아대학교

References

  1. H. Yamashita, N. Ohno, Y. Hashimoto, M. Inoue, and K. Akita, MSJ, Vol. J16-B, 729 (1978)
  2. Y. Hashimoto, K. Ishino, and H. Kurihara, EMCJ, 88-6, 37 (1988)
  3. 淸水康敬, 杉浦行, 石野建, 電磁波の吸收と遮蔽, 日經技術圖書株 式會社, 4 (1989)
  4. 강근덕, 새로운 전자파 장해관련 기준 제/개정, 전파진흥지, 11 (1996)
  5. L. B. Gravelle and P. F. Wilson, IEEE Trans. EMC, 34, 109 (1992) https://doi.org/10.1109/15.135623
  6. R. Laroussi and G. I. Costache, IEEE Trans. EMC, 35, 178 (1993) https://doi.org/10.1109/15.229423
  7. Y. Kotsuka, MSJ, 21, 1159 (1997)
  8. L. I. Im, C. W. Kim, and T. S. Oh, J. Korea Ceramic Society, 36, 571 (1999)
  9. 內藤喜之, 電波吸收體, オー厶社, 104 (1987)
  10. 石野 健, 橋本康雄, ニューセラミックスの發展, 91 (1985)
  11. 平賀 貞太郎, 尾島 輝彦, 奥谷 克伸, フエライト(電子材料シリ─ ズ), 丸善, 100 (1987)
  12. J. W. Joung and W. J. Lee, J. Korean Magnetics Society, 5, 947 (1995)
  13. Y.-R. Wang and S.-F. Wang, Internatinal J. of Inorganic Materials,3, 1189 (2001) https://doi.org/10.1016/S1466-6049(01)00123-4
  14. H. Saita, Y. Fang, A. Nakano, D. Agrawal, M. T. Lanagan, T. R. Shrout, and C. A. Randall, Jpn. J. Appl. Phys., 41, 86 (2002) https://doi.org/10.1143/JJAP.41.86
  15. 近角總信, 太田惠造, 安違健五, 津屋昇, 石川義和, 磁性體ハンド ボック, 朝倉 (1987)
  16. W. Heiser, J. Appl. Phys., 30, 22 (1959) https://doi.org/10.1063/1.1734966
  17. H. Igarshi and K. Okazaki, JACS, 60, 51 (1977)
  18. J. Smit and H. P. J. Wijn, Ferrites, Philips' Tech. Library, 268 (1965)
  19. J. K. Watson, Applications of Magnetism, John Wiley & Sons, 232 (1980)
  20. H. M. Musal Jr. and D. C. Smith, IEEE Trans. on Magnetics, 26, 1462 (1990) https://doi.org/10.1109/20.104411