Abstract
EAF reduction slag has unstable properties of expansion and destruction. Therefore, it cannot be used as a construction material. The purpose of this study was to use EAF reduction slag as a concrete admixture. EAF reduction slag contains $11CaO{\cdot}7Al_2O_3{\cdot}CaF_2$ and ${\beta}-C_2S$ (calcium aluminate compounds). To confirm the properties of EAF reduction slag as a concrete admixture, the condensation, compressive strength and activity factor due to substitution rate of EAF reduction slag were measured. Originally, EAF reduction slag was cured rapidly because of its chemical composition ($11CaO{\cdot}7Al_2O_3{\cdot}CaF_2$). On the other hand, when 8% gypsum was added, its properties of condensation and compressive strength were similar to the plain specimen. When 6% gypsum was added, the quality of the KS F 2536 standards (quality standard number 3) were met in terms of activity factor. Overall, 8% gypsum addition is the most appropriate by considering the activity factor in the long-term compressive strength.
본 전기로 환원슬래그는 팽창성 물질이 함유되어 불안정한 상태이므로 건설용 재료로 그대로 사용하기에는 다소 무리가 있다. 그러나 전기로 환원슬래그에는 $11CaO{\cdot}7Al_2O_3{\cdot}CaF_2$와 ${\beta}-C_2S$ (calcium aluminate compounds) 물질이 함유되어 있으므로 적절한 성분 보조제를 혼합하여 사용한다면 콘크리트용 혼화재료로서 사용이 가능할 것으로 판단된다. 이에 본 연구에서는 콘크리트 혼화재료서 전기로환원슬래그 미분말의 사용 가능성을 검토하고자 한다. 전기로 환원슬래그 미분말의 치환율별 모르타르 강도특성과 응결특성을 검토 결과, 최적 치환율은 30% 수준으로 나타났다. 최적 치환율에 석고 첨가에 따른 응결시간 및 강도특성을 파악한 결과, 전기로환원슬래그 미분말 치환율 30%인 배합에 이수석고를 8% 혼입하였을 경우 압축강도 발현 성상 및 응결특성이 OPC와 유사한 결과를 나타내었다.