Advances in concrete construction

Techno-Press (테크노프레스)
권호 표지
DOI QR코드

DOI QR Code

Interface characteristics of concrete prepared with recycled aggregates by heating

  • Xiaohui Yan (Shanghai Urban Construction Vocational College) ;
  • Xiaonan Zhang (Xianyang Normal University) ;
  • JiaYuan Wang (China Construction Seventh Engineering Division. Corp. LTD) ;
  • Ruihua Yang (Shanghai Urban Construction Vocational College)
  • Received : 2025.02.16
  • Accepted : 2025.06.17
  • Published : 2025.08.25
⟨ Previous Next ⟩

Abstract

This study investigates the effects of heating temperature and water-to-binder ratio (W/B) on the interfacial transition zones (ITZ) in recycled concrete, with a focus on multiple interfaces, including the interface between old aggregate and new mortar (LG-XJ), the interface between old aggregate and old mortar (LG-LJ), and the interface between old mortar and new mortar (LJ-XJ). The results show that heating temperature significantly impacts the ITZ microstructure and mechanical properties. Lower temperatures (300℃ and 500℃) promote dehydration of old mortar, leading to denser ITZ structures with increased interfacial hardness and reduced transition zone widths. Conversely, at 700℃, decomposition of hydration products increases porosity and microcracking, resulting in decreased interfacial hardness and wider transition zones. Similarly, higher W/B ratios lead to insufficient cement hydration, increased porosity, and looser ITZ microstructures, thereby reducing interfacial microhardness and widening the ITZ. SEM analysis further reveals distinct microstructural characteristics among the interfaces, with the LJ-XJ interface exhibiting better density and uniformity compared to the LG-XJ interface after heat treatment. These findings highlight the importance of optimizing heating temperature and W/B ratio to enhance the interfacial properties and overall performance of recycled concrete.

Keywords

Acknowledgement

The authors acknowledge the financial support of the Science and Technology Research Project of Henan Province (No. 252102230050) and the Prefabricated Building Research Institute of Anhui Province (No. AHZPY2022KF02).

References

  1. Al-Bayati, H.K.A., Das, P.K., Tighe, S.L. and Baaj, H. (2016), "Evaluation of various treatment methods for enhancing the physical and morphological properties of coarse recycled concrete aggregate", Constr. Build. Mater., 112, 284-298. http:/doi.org/10.1016/j.conbuildmat.2016.02.176
  2. Bravo, M., De Brito, J., Pontes, J. and Evangelista, L. (2015), "Durability performance of concrete with recycled aggregates from construction and demolition waste plants", Constr. Build. Mater., 77, 357-369. http://doi.org/10.1016/j.conbuildmat.2014.12.103
  3. Bru, K., Touzé, S., Bourgeois, F., Lippiatt, N. and Ménard, Y. (2014), "Assessment of a microwave-assisted recycling process for the recovery of high-quality aggregates from concrete waste", Int. J. Mineral Process., 126, 90-98. http://doi.org/10.1016/j.minpro.2013.11.009
  4. Chen, S., Kwan, A.K.H. and Yue, Z.Q. (2013), "Actual microstructure-based numerical method for mesomechanics of concrete", Comput. Concrete, Int. J., 12(1), 1-18. https://doi.org/10.12989/cac.2013.12.1.001
  5. Feng, C., Cui, B., Ge, H., Huang, Y., Zhang, W. and Zhu, J. (2021), "Reinforcement of recycled aggregate by Microbial-Induced mineralization and deposition of calcium carbonate—Influencing factors, mechanism and effect of reinforcement", Crystals, 11(8), p. 887. http://doi.org/10.3390/cryst11080887
  6. Guo, Z., Zhou, L., Sun, Q., Gao, Z., Miao, Q. and Ding, H. (2023), "Sustainable SCC with high volume recycled concrete aggregates and SCMs for improved mechanical and environmental performances", Adv. Concrete Constr., Int. J., 16(6), 303-316. https://doi.org/10.12989/acc.2023.16.6.303
  7. Gupta, T., Saraswat, V. and Meesala, C.R. (2024), "Effect of recycled aggregate on properties of blended geopolymer concrete cured at ambient temperature", Adv. Concrete Constr., Int. J., 18(3), 191-204. https://doi.org/10.12989/acc.2024.18.3.191
  8. Kareem, M.A. and Hilal, A.A. (2023), "Effect of waste glass as powder and aggregate on strength and shrinkage of fiber reinforced foam concrete", Adv. Mater. Res., Int. J., 12(4), 331-349. https://doi.org/10.12989/amr.2023.12.4.331
  9. Katz, A. (2004), "Treatments for the improvement of recycled aggregate", J. Mater. Civil Eng., 16(6), 597-603. http://doi.org/10.1061/(ASCE)0899-1561(2004)16:6(597)
  10. Kou, S.C. and Poon, C.S. (2010), "Properties of concrete prepared with PVA-impregnated recycled concrete aggregates", Cement Concrete Compos., 32(8), 649-654. http://doi.org/10.1016/j.cemconcomp.2010.05.003
  11. Kurbetci, Ş., Nas, M. and Şahin, M. (2022), "Durability properties of mortars with fly ash containing recycled aggregates", Adv. Concrerte Constr., Int. J., 13(1), 101-111. https://doi.org/10.12989/acc.2022.13.1.101
  12. Leemann, A., Münch, B., Gasser, P. and Holzer, L. (2006), "Influence of compaction on the interfacial transition zone and the permeability of concrete", Cement Concrete Res., 36(8), 1425-1433. http://doi.org/10.1016/j.cemconres.2006.02.010
  13. Li, W., Xiao, J., Sun, Z., Kawashima, S. and Shah, S.P. (2012), "Interfacial transition zones in recycled aggregate concrete with different mixing approaches", Constr. Build. Mater., 35, 1045-1055. http://doi.org/10.1016/j.conbuildmat.2012.06.022
  14. Li, Q.Y., Wang, Z.X., Yue, G.B., and Cao, Y.B. (2017), "Effect of chloride erosion on multiple interfacial microstructure of recycled concrete", Bull. Silicate, 36(01), 27-32. http://doi.org/10.16552/j.cnki.issn1001-1625.2017.01.005
  15. Lotfi, S., Eggimann, M., Wagner, E., Mróz, R. and Deja, J. (2015), "Performance of recycled aggregate concrete based on a new concrete recycling technology", Constr. Build. Mater., 95, 243-256. http://doi.org/10.1016/j.conbuildmat.2015.07.021
  16. Lu, C., Yu, Q., Wei, J., Niu, Y., Zhang, Y., Lin, C., Chen, P., Shi, C. and Yang, P. (2024), "Influence of interface transition zones (ITZ) and pore structure on the compressive strength of recycled aggregate concrete", Constr. Build. Mater, 456, p. 139299. http://doi.org/10.1016/j.conbuildmat.2024.139299
  17. Mičušík, M., Bonnefond, A., Paulis, M. and Leiza, J.R. (2012), "Synthesis of waterborne acrylic/clay nanocomposites by controlled surface initiation from macroinitiator modified montmorillonite", Eur. Polymer J., 48(5), 896-905. http://doi.org/10.1016/j.eurpolymj.2012.03.002
  18. Mohamed, A.Y., Canpolat, O. and Al-Mashhadani, M.M. (2022), "Mechanical and durability of geopolymer concrete containing fibers and recycled aggregate", Comput. Concrete, Int. J., 30(6), 421-432. https://doi.org/10.12989/cac.2022.30.6.421
  19. Mukharjee, B.B. and Barai, S.V. (2019), "Performance assessment of nano-Silica incorporated recycled aggregate concrete", Adv. Concrete Constr., Int. J., 8(4), 321-333. https://doi.org/10.12989/acc.2019.8.4.321
  20. Shohana, S.A., Hoque, M.I. and Sobuz, M.H. (2020), "Experimental investigation on hardened properties of recycled coarse aggregate concrete", Adv. Concrete Constr., Int. J., 10(5), 369-379. https://doi.org/10.12989/acc.2020.10.5.369
  21. Silva, R.V., De Brito, J. and Dhir, R.K. (2015), "Prediction of the shrinkage behavior of recycled aggregate concrete: A review", Constr. Build. Mater., 77, 327-339. http://doi.org/10.1016/j.conbuildmat.2014.12.102
  22. Su, Y., Gu, S., Chang, X.L. and Li, J.X. (2015), "Experimental study on heating modified recycled concrete coarse aggregate", Concrete Cement Products, 2015(10), 6-10. https://doi.org/10.19761/j.1000-4637.2015.10.002 [In Chinese]
  23. Tam, V.W., Tam, C.M. and Le, K.N. (2007), "Removal of cement mortar remains from recycled aggregate using pre-soaking approaches", Resour. Conserv. Recycl., 50(1), 82-101. http://doi.org/10.1016/j.resconrec.2006.05.012
  24. Verma, S.K. and Ashish, D.K. (2017), "Mechanical behavior of concrete comprising successively recycled concrete aggregates", Adv. Concrete Constr., Int. J., 5(4), 303-311. https://doi.org/10.12989/acc.2017.5.4.303
  25. Xiao, J.Z., Liu, Q., Li, W.G. and Tam, V. (2009), "Study on fine microstructure and failure Mechanism of recycled concrete", J. Qingdao Univ. Technol., 30(4), 24-30.