The Effect of Deuterium Injection to Amorphous $Fe_{90}Zr_{10}$

비정질 $Fe_{90}Zr_{10}$의 중수소 주입효과

Deuterium was injected into melt-spun ribbons of ${\alpha}-Fe_{90}Zr_{10}$ using the electrolytic hydrogenation method, and the magnetic properties of these ${\alpha}-D_{x}Fe_{90}Zr_{10}$ ribbons were studied. By comparing these results with those of ${\alpha}-H_{x}Fe_{91}Zr_{9}$, the effects of phonons to magnetic properties were investigated. The Curie temperature $T_{c}$, and the spontaneous magnetizations of the $D_{47}Fe_{90}Zr_{10}$ and the $Fe_{90}Zr_{10}$ were studied using the Mbssbauer spectroscopy. From these investigations, it was found that the Curie temperature of $D_{x}Fe_{90}Zr_{10}$ was 75K higher than that of $Fe_{90}Zr_{10}$. It was believed that this indicated the importance of local deformation to the amorphous magnetism. Also by comparing the spontaneous magnetizations of $D_{47}Fe_{90}Zr_{10}$ with those of $Fe_{90}Zr_{10}$ as a function of temperature, it was found that the deuterium injection reduced the fluctuation of exchange integral.

melt-spinning 방법에 의해 제조된 비정질 $Fe_{90}Zr_{10}$ ribbon에 전해수소화 반응법에 의해 증수소를 주입하였다. 중수소가 주입된 $D_{x}Fe_{90}Ze_{10}$계의 자기적 성질에 대하여 연구 하였다. 이 결과와 이미 보고된 수소가 주입된 $H_{x}Fe_{91}Zr_{9}$계의 결과와 비교하여 자기적인 성질에 미치는 phonon의 효과에 대하여 연구하였다. 또한 $M\"{o}ssbauer$분광법을 이용하여 Curie온도 $T_{c}$를 조사한 결과 중수소가 주입되기 전 시료의 $T_{c}$보다 75K 상승하였는데, 이는 수소 주위의 local de-formation에 의한 것으로 보인다. 그리고 $M\"{o}ssbauer$분광법에서 얻은 $D_{47}Fe_{90}Zr_{10}$의 자발 자율화을 온도의 함수로 표시하여, 중수소를 주입하지 않은 $Fe_{90}Zr_{10}$의 자발 자화율과 비교한 결과 중수소 주입시 교환 상호작용의 요동이 줄어듬이 확인되었다.